Glass transition temp.(Tg) :DSC |
- |
Glass transition temp.(Tg) :TMA (°C) |
- |
Glass transition temp.(Tg) :TMA
Measurement in tensile mode (°C) |
240 |
Glass transition temp.(Tg) :DMA (°C) |
- |
Glass transition temp.(Tg) :DMA
Measurement in tensile mode (°C) |
270 |
Thermal decomposition temp.(Td):TGA (°C) |
390 |
Time to delam(T288)Without Cu:IPC-TM-650 2.4.24.1 (min) |
>120 |
Time to delam(T288)With Cu:IPC-TM-650 2.4.24.1 (min) |
>120 |
CTE:α1,X-axis,IPC-TM-650 2.4.24 (ppm/°C) |
8-10 *1 |
CTE:α1,Y-axis,IPC-TM-650 2.4.24 (ppm/°C) |
8-10 *1 |
CTE:α1,Z-axis,IPC-TM-650 2.4.24 (ppm/°C) |
22 |
CTE:α2,Z-axis,IPC-TM-650 2.4.24 (ppm/°C) |
95 |
Thermal conductivity:Laser flash,25˚C (W/m·K) |
0.7 |
Volume resistivity:IPC-TM-650 2.5.17.1,C-96/35/90 (MΩ·cm) |
1 x 10⁹ |
Surface resistivity:IPC-TM-650 2.5.17.1,C-96/35/90 (MΩ) |
1 x 10⁸ |
Dielectric constant(Dk)@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 |
4.7 |
Dielectric constant(Dk)@10GHz:IPC-TM-650 2.5.5.5,C-24/23/50 |
- |
Dielectric constant(Dk)@12GHz:Balanced-type circular disk resonator,C-24/23/50 |
- |
Dissipation factor(Df )@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 |
0.011 |
Dissipation factor(Df )@10GHz:IPC-TM-650 2.5.5.5,C-24/23/50 |
- |
Dissipation factor(Df )@12GHz:Balanced-type circular disk resonator,C-24/23/50 |
- |
Water absorption:IPC-TM-650 2.6.2.1,D-24/23 (%) |
0.3 |
Flexural modulus,Warp/MD:JIS C 6481 (GPa) |
35 |
Flexural modulus,Fill/TD:JIS C 6481 (GPa) |
33 |
Peel strength,1oz:IPC-TM-650 2.4.8 (kN/m (lb/inch)) |
0.9(5.1)
(12μm) |
Flammability:UL,C-48/23/50 |
94V-0 |
The sample thickness |
The sample thickness is depending on the test method. |
The above data are typical values and not guaranteed values. |
- |
*1 Test method: TMA |
- |