R-5775(G)/R-5670(G) : Multi-layer Circuit Board Materials for ICT infrastructure equipment "MEGTRON" series

Product
Multi-layer Circuit Board Materials for ICT infrastructure equipment "MEGTRON" series

Series/Type
MEGTRON6 series Ultra-low transmission loss Highly heat resistant Multi-layer circuit board materials

Parts no
R-5775(G)/R-5670(G)

Zoom
Photo:R-5775(G)/R-5670(G)
Item Performance characteristics
Glass transition temp.(Tg) :DSC (°C) 185
Glass transition temp.(Tg) :TMA (°C) -
Glass transition temp.(Tg) :DMA (°C) 210
Thermal decomposition temp.(Td):TGA (°C) 410
Time to delam(T288)Without Cu:IPC-TM-650 2.4.24.1 (min) >120
Time to delam(T288)With Cu:IPC-TM-650 2.4.24.1 (min) >120
CTE:α1,X-axis,IPC-TM-650 2.4.24 (ppm/°C) 14-16
CTE:α1,Y-axis,IPC-TM-650 2.4.24 (ppm/°C) 14-16
CTE:α1,Z-axis,IPC-TM-650 2.4.24 (ppm/°C) 45
CTE:α2,Z-axis,IPC-TM-650 2.4.24 (ppm/°C) 260
Thermal conductivity:Laser flash,25˚C (W/m·K) 0.42
Volume resistivity:IPC-TM-650 2.5.17.1,C-96/35/90 (MΩ·cm) 1 x 10⁹
Surface resistivity:IPC-TM-650 2.5.17.1,C-96/35/90 (MΩ) 1 x 10⁸
Dielectric constant(Dk)@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 3.7
Dielectric constant(Dk)@10GHz:IPC-TM-650 2.5.5.5,C-24/23/50 -
Dielectric constant(Dk)@12GHz:Balanced-type circular disk resonator,C-24/23/50 3.6
Dielectric constant(Dk)@14GHz:Balanced-type circular disk resonator,C-24/23/50 -
Dissipation factor(Df )@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 0.002
Dissipation factor(Df )@10GHz:IPC-TM-650 2.5.5.5,C-24/23/50 -
Dissipation factor(Df )@12GHz:Balanced-type circular disk resonator,C-24/23/50 0.004
Dissipation factor(Df)@14GHz:Balanced-type circular disk resonator,C-24/23/50 -
Water absorption:IPC-TM-650 2.6.2.1,D-24/23 (%) 0.14
Flexural modulus,Warp/MD:JIS C 6481 (GPa) 20
Flexural modulus,Fill/TD:JIS C 6481 (GPa) 19
Peel strength,1oz:IPC-TM-650 2.4.8 (kN/m (lb/inch)) 0.8(4.6)
(Cu:H-VLP)
Peel Strength,1oz(H-VLP3):IPC-TM-650 2.4.8 (kN/m) -
Flammability:UL,C-48/23/50 94V-0
The sample thickness 0.75mm
The above data are typical values and not guaranteed values. -
*1 Test method: TMA -