| Glass transition temp.(Tg) :DSC (°C) |
140 |
| Glass transition temp.(Tg) :TMA (°C) |
140 |
| Glass transition temp.(Tg) :DMA (°C) |
150 |
| Thermal decomposition temp.(Td):TGA (°C) |
315 |
| Thermal decomposition temp.(Td):TG/DTA (°C) |
- |
| Time to delam(T288)Without Cu:IPC-TM-650 2.4.24.1 (min) |
5 |
| Time to delam(T288)With Cu:IPC-TM-650 2.4.24.1 (min) |
1 |
| CTE:α1,X-axis,IPC-TM-650 2.4.24 (ppm/°C) |
11–13 |
| CTE:α1,X-axis,IPC-TM-650 2.4.41 (ppm/°C) |
- |
| CTE:α1,Y-axis,IPC-TM-650 2.4.24 (ppm/°C) |
13–15 |
| CTE:α1,Y-axis,IPC-TM-650 2.4.41 (ppm/°C) |
- |
| CTE:α1,Z-axis,IPC-TM-650 2.4.24 (ppm/°C) |
65 |
| CTE:α2,Z-axis,IPC-TM-650 2.4.24 (ppm/°C) |
270 |
| Volume resistivity:IPC-TM-650 2.5.17.1,C-96/35/90 (MΩ·cm) |
1 x 10⁹ |
| Surface resistivity:IPC-TM-650 2.5.17.1,C-96/35/90 (MΩ) |
1 x 10⁸ |
| Dielectric constant(Dk)@1MHz:IPC-TM-650 2.5.5.9,C-24/23/50 |
4.6 |
| Dielectric constant(Dk)@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 |
4.3 |
| Dissipation factor(Df )@1MHz:IPC-TM-650 2.5.5.9,C-24/23/50 |
0.014 |
| Dissipation factor(Df )@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 |
0.016 |
| Water absorption:IPC-TM-650 2.6.2.1,D-24/23 (%) |
0.14 |
| Peel strength,1oz:IPC-TM-650 2.4.8 (kN/m) |
2 |
| Flammability:UL,C-48/23/50 |
94V-0 |
| Volume resistivity:C-96/20/65 |
- |
| Volume resistivity:C-96/20/65+C-96/40/90 |
- |
| Surface resistivity:C-96/20/65 |
- |
| Surface resistivity:C-96/20/65+C-96/40/90 |
- |
| Insulation resistance:C-96/20/65 |
- |
| Insulation resistance:C-96/20/65+D-2/100 |
- |
| Dielectric constant (Dk)1MHz:JIS C-96/20/65 |
- |
| Dielectric constant (Dk)1MHz:C-96/20/65+D-24/23 |
- |
| Dissipation factor (Df)1MHz:C-96/20/65 |
- |
| Dissipation factor (Df)1MHz:C-96/20/65+D-24/23 |
- |
| Solder heat resistance (260°C) |
- |
Peel strength,Copper foil:0.018mm
(18μm),A |
- |
Peel strength,Copper foil:0.018mm
(18μm),S₄ |
- |
Peel strength,Copper foil:0.035mm
(35μm),A |
- |
Peel strength,Copper foil:0.035mm
(35μm),S₄ |
- |
| Heat resistance |
- |
| Flexural strength:Fill |
- |
| Water absorption:E-24/50+D-24/23 |
- |
| Flammability: |
- |
| Alkali resistance:dipping (3min) |
- |
| The sample thickness |
32mil(0.8mm) |
| The above data are typical values and not guaranteed values. |
- |