Flexible Circuit Board Materials for Mobile Products "FELIOS" series : Models

Found 121 matches of 121
페이지 당 건수
Only the selected models
Choice Parts no Catalog /
Datasheet
Series/Type Copper Foil Type Copper Foil Part No. Copper Foil Thickness
(µm)
Fiim Thickness
(µm)
Total products thickness
(µm)
Peel Strength.90°:JIS C 6471.A
(mm)
Peel Strength.90°:JIS C 6471.260℃ Solder 5sec
(mm)
Dimensional Stability.MD:IPC-TM-650.After Etching
(%)
Dimensional Stability.TD:IPC-TM-650.After Etching
(%)
Dimensional Stability.MD:IPC-TM-650.E-0.5/150
(%)
Dimensional Stability.TD:IPC-TM-650.E-0.5/150
(%)
Soldering Resistance:JIS C 6471.A
(°C)
Soldering Resistance:JIS C 6471.C-96/40/90
(°C)
MIT Test:JIS C 6471.0.38R×4.9N,MD MIT Test:JIS C 6471.0.38R×4.9N,TD Tensile Modulus:IPC-TM-650
(GPa)
Coefficient of Thermal Expansion.MD:TMA 100℃→250℃,
5℃/min
(ppm/K)
Coefficient of Thermal Expansion.TD:TMA 100℃→250℃,
5℃/min
(ppm/K)
Dielectric Constant at 1MHz:IPC-TM-650 2.5.5.5.A Dielectric Constant at 2GHz:IPC-TM-650 2.5.5.5.A Dielectric Constant at 10GHz:Cavity resonance.A Dissipation Factor at 1MHz:IPC-TM-650 2.5.5.5.A Dissipation Factor at 2GHz:IPC-TM-650 2.5.5.5.A Dissipation Factor at 10GHz:Cavity resonance.A Insulation resistance:JIS C 6471.A
(Ω)
Insulation resistance:JIS C 6471.C-96/40/90
(Ω)
Water absorption.IPC-TM-650:JIS C 6471.D-24/23
(%)
Water absorption:JIS C 6471.D-24/23
(%)
Moisture Absorption.IPC-TM-650:C-24/23/50
(%)
Tg:DMA.A
(°C)
Flammability:UL 94.A+E-168/70 * These are observed data, not guaranteed performance.
The test method of above item is determined according to Panasonic internal standard.
Glass transition temp.(Tg) :TMA(Ad)
(°C)
Glass transition temp.(Tg) :DMA
Measurement in tensile mode(Ad)
(°C)
CTE:α1,X-axis,IPC-TM-650 2.4.24
(ppm/°C)
CTE:α1,Y-axis,IPC-TM-650 2.4.24
(ppm/°C)
CTE:α1,Z-axis,IPC-TM-650 2.4.24
(ppm/°C)
CTE:α2,Z-axis,IPC-TM-650 2.4.24
(ppm/°C)
Volume resistivity:IPC-TM-650 2.5.17.1,C-96/35/90
(MΩ·cm)
Dielectric constant(Dk)@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 (Ad) Dissipation factor(Df )@1GHz:IPC-TM-650 2.5.5.9,C-24/23/50 (Ad) Water absorption:IPC-TM-650 2.6.2.1,D-24/23
(%)
Peel strength,1oz:IPC-TM-650 2.4.8
(kN/m (lb/inch))
Flammability:UL,A+E-168/70 The sample thickness *1 Condition: C-96/20/65, Unit : MΩ·m *2 Condition: E-24/50+D-24/23 *3 Measured by R-FR10/R-F775 25μm/ R-FR10 construction
R-FR10
R-FR10 (FRCC) - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - - 190 210 80(Ad) 80(Ad) 80(Ad) 580(Ad) 1 x 10<sup>8</sup> *2 3 0.019 1.2 *4 0.8(4.6)
(ED:12μm)
94VTM-0 *5 0.032mm
(Cu:12μm, PI:5μm,Ad:15μm)
- - -
R-F775_B4EV_9-150-9(ED)
R-F775 (Double-sided copper clad) ED VLP 9 150 168 - - - - - - 330 250 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_B2RB_18-150-18(RA)
R-F775 (Double-sided copper clad) RA BHY 18 150 186 1.6 1.6 -0.023 -0.025 -0.081 -0.062 330 250 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_B1RB_35-150-35(RA)
R-F775 (Double-sided copper clad) RA BHY 35 150 220 1.6 1.6 -0.048 -0.035 -0.081 -0.066 330 250 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_A4EV_9-125-9(ED)
R-F775 (Double-sided copper clad) ED VLP 9 125 143 - - - - - - 330 250 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_A3EV_12-125-12(ED)
R-F775 (Double-sided copper clad) ED VLP 12 125 149 1.5 1.5 -0.0163 -0.0141 -0.04 -0.0401 330 250 5 7 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_A2RB_18-125-18(RA)
R-F775 (Double-sided copper clad) RA BHY 18 125 161 2 2 -0.015 -0.012 -0.076 -0.044 330 250 9 10 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_A1RB_35-125-35(RA)
R-F775 (Double-sided copper clad) RA BHY 35 125 195 1.6 1.6 -0.033 -0.023 -0.059 -0.053 330 250 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_A0RB_70-125-70(RA)
R-F775 (Double-sided copper clad) RA BHY 70 125 265 2.5 2.5 -0.0192 -0.0299 -0.0548 -0.0684 330 250 9 10 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_5PEL_2-12.5-2(ED)
R-F775 (Double-sided copper clad) ED MT18FL 2 12.5 16.5 1.3 1.3 0.0164 0.0443 0.0146 0.0413 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 VTM-0 - - - - - - - - - - - - - - - - -
R-F775_56ES_6-12.5-6(ED)
R-F775 (Double-sided copper clad) ED SEED 6 12.5 24.5 1 1 0.017 0.06 0.005 0.053 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 VTM-0 - - - - - - - - - - - - - - - - -
R-F775_54RS_9-12.5-9(RA)
R-F775 (Double-sided copper clad) RA BHYA-HS 9 12.5 31 1 1 0.003 0.033 -0.007 0.025 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 VTM-0 - - - - - - - - - - - - - - - - -
R-F775_54EF_9-12.5-9(ED)
R-F775 (Double-sided copper clad) ED F2WS 9 12.5 30.5 1 1 0.03 0.059 0.025 0.059 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 VTM-0 - - - - - - - - - - - - - - - - -
R-F775_53RX_12-12.5-12(RA
R-F775 (Double-sided copper clad) RA BHYX-T 12 12.5 37 1 1 0.021 0.035 0.009 0.028 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 VTM-0 - - - - - - - - - - - - - - - - -
R-F775_53EF_12-12.5-12(ED
R-F775 (Double-sided copper clad) ED F2WS 12 12.5 36.5 1 1 0.0235 0.0574 0.0092 0.0562 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 VTM-0 - - - - - - - - - - - - - - - - -
R-F775_52RB_18-12.5-18(RA
R-F775 (Double-sided copper clad) RA BHY 18 12.5 48.5 1.2 1.2 0.0436 0.0228 0.0169 -0.0084 330 260 530 550 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 VTM-0 - - - - - - - - - - - - - - - - -
R-F775_52EF_18-12.5-18(ED
R-F775 (Double-sided copper clad) ED F2WS 18 12.5 48.5 1 1 0.016 0.0598 0.0012 0.0464 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 VTM-0 - - - - - - - - - - - - - - - - -
R-F775_51RB_35-12.5-35(RA
R-F775 (Double-sided copper clad) RA BHY 35 12.5 82.5 1.6 1.6 0.006 0.027 -0.013 0.011 330 260 120 120 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 VTM-0 - - - - - - - - - - - - - - - - -
R-F775_44EV_9-100-9(ED)
R-F775 (Double-sided copper clad) ED VLP 9 100 118 1.5 1.5 -0.0099 -0.0023 -0.0255 -0.0165 330 250 9 7 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_43RX_12-100-12(RA)
R-F775 (Double-sided copper clad) RA BHYX-T 12 100 124 1.5 1.5 0.015 0.012 -0.006 -0.002 330 250 20 20 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_43EV_12-100-12(ED)
R-F775 (Double-sided copper clad) ED VLP 12 100 124 2.4 2.4 -0.012 -0.014 -0.029 -0.03 330 250 10 10 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_42RB_18-100-18(RA)
R-F775 (Double-sided copper clad) RA BHY 18 100 136 2.2 2.2 0.004 0.003 -0.04 -0.28 330 250 10 15 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_42EV_18-100-18(ED)
R-F775 (Double-sided copper clad) ED VLP 18 100 136 2.6 2.6 -0.011 -0.014 -0.029 -0.037 330 250 10 10 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_41RB_35-100-35(RA)
R-F775 (Double-sided copper clad) RA BHY 35 100 170 2.5 2.5 -0.01 -0.005 -0.039 -0.037 330 250 15 15 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_41EM_35-100-35(ED)
R-F775 (Double-sided copper clad) ED T4M-HDR 35 10 170 3 3 -0.0151 -0.0249 -0.0447 -0.064 330 250 12 12 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_40RB_70-100-70(RA)
R-F775 (Double-sided copper clad) RA BHY 70 100 240 2.5 2.5 -0.0457 -0.0254 -0.0774 -0.0567 330 250 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_3PEL_2-75-2(ED)
R-F775 (Double-sided copper clad) ED MT18FL 2 75 79 1.3 1.3 -0.0132 -0.0057 -0.0507 -0.0383 330 250 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_34EV_9-75-9(ED)
R-F775 (Double-sided copper clad) ED VLP 9 75 93 1.5 1.5 -0.007 0.0012 -0.0343 -0.0293 330 250 35 39 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_33RX_12-75-12(RA)
R-F775 (Double-sided copper clad) RA BHYX-T 12 75 99 1.5 1.5 -0.002 0.01 -0.037 -0.021 330 250 20 30 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_33EV_12-75-12(ED)
R-F775 (Double-sided copper clad) ED VLP 12 75 99 1.5 1.5 -0.038 -0.005 -0.083 -0.035 330 250 16 15 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_32RB_18-75-18(RA)
R-F775 (Double-sided copper clad) RA BHY 18 75 111 1.6 1.6 0.001 0.009 -0.017 -0.009 330 250 19 26 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_32EVY_18-75-18(ED)
R-F775 (Double-sided copper clad) ED VLP 18 75 111 1.5 1.5 -0.015 -0.004 0.035 0.031 330 250 16 15 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_31RB_35-75-35(RA)
R-F775 (Double-sided copper clad) RA BHY 35 75 145 1.8 1.78 -0.013 0.004 -0.036 -0.015 330 250 20 25 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_31EM_35-75-35(ED)
R-F775 (Double-sided copper clad) ED T4M-HDR 35 70 145 2.5 2.5 -0.034 -0.025 -0.067 -0.058 330 250 20 20 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_30RB_70-75-70(RA)
R-F775 (Double-sided copper clad) RA BHY 70 75 215 2.5 2.5 -0.0269 -0.0019 -0.0542 -0.0296 330 250 18 20 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_2PEL_2-50-2(ED)
R-F775 (Double-sided copper clad) ED MT18FL 2 50 54 1.3 1.3 -0.02 -0.006 -0.058 -0.05 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_27RN_105-50-105(RA
R-F775 (Double-sided copper clad) RA BHY-HA-V2 105 50 260 3 3 -0.0106 -0.027 -0.0518 -0.062 330 250 26 26 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_26ES_6-50-6(ED)
R-F775 (Double-sided copper clad) ED SEED 6 50 62 1 1 0.024 0.027 -0.002 0.009 330 260 40 40 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_24RS_9-50-9(RA)
R-F775 (Double-sided copper clad) RA BHYA-HS 9 50 68 1.2 1.2 -0.01 0.002 -0.036 -0.026 330 260 30 16 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_24EV_9-50-9(ED)
R-F775 (Double-sided copper clad) ED VLP 9 50 68 1.7 1.7 -0.015 0.022 -0.033 -0.008 330 260 40 40 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_23RX_12-50-12(RA)
R-F775 (Double-sided copper clad) RA BHYX-T 12 50 74 1.3 1.3 -0.011 -0.008 -0.022 -0.017 330 260 46 60 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_23EV_12-50-12(ED)
R-F775 (Double-sided copper clad) ED VLP 12 50 74 1.7 1.7 0.002 0.01 -0.021 -0.019 330 260 40 40 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_22RB_18-50-18(RA)
R-F775 (Double-sided copper clad) RA BHY 18 50 86 1.5 1.5 0.0233 0.0069 0.0072 0.0072 330 260 60 60 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_22EV_18-50-18(ED)
R-F775 (Double-sided copper clad) ED VLP 18 50 86 1.6 1.6 0.009 0.02 0.0082 0.013 330 260 35 35 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_21RB_35-50-35(RA)
R-F775 (Double-sided copper clad) RA BHY 35 50 120 1.5 1.6 0.0222 0.0286 0.019 0.001 330 260 35 40 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_21EM_35-50-35(ED)
R-F775 (Double-sided copper clad) ED T4M-HDR 35 50 120 2.5 2.5 -0.018 0.018 -0.038 -0.001 330 260 45 40 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_20RB_70-50-70(RA)
R-F775 (Double-sided copper clad) RA BHY 70 50 190 1.1 1.1 -0.044 -0.011 -0.082 -0.046 330 260 26 26 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_1PEL_2-25-2(ED)
R-F775 (Double-sided copper clad) ED MT18FL 2 25 29 1.3 1.3 -0.035 0.001 -0.041 -0.007 330 260 - - 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_17RN_105-25-105(RA
R-F775 (Double-sided copper clad) RA BHY-HA-V2 105 25 235 1.5 1.5 -0.0164 0.0122 -0.0523 -0.0193 330 260 34 31 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -
R-F775_16ES_6-25-6(ED)
R-F775 (Double-sided copper clad) ED SEED 6 25 37 1 1 -0.004 0.009 -0.024 0.002 330 260 170 170 7.1 19.3 17.3 3.2 3.2 - 0.002 0.002 - >1.0×10^14 >1.0×10^14 0.8 - 0.7 350 V-0 - - - - - - - - - - - - - - - - -